HORDA 410NiMo
ISO 14343 A/B:
W 13 4
AWS A5.9:
ER 410 NiMo
ГОСТ 2246-70:
GTAW low-carbon rods of the 12% Cr,4.5% Ni, 0.5% Mo type. HORDA 410NiMo is used for welding soft-martentsitic and martensitic-ferritic steels in different applications, such as hydro turbines. Designed with precisely tuned alloying composition creating a weld deposit featuring very good ductility, CVN toughness and crack resistance despite its higher strength
Typical chemical composition
| C | Si | Mn | S | P | Cr | Ni | Mo |
| <0,020 | 0,45 | 0,60 | 0,010 | 0,015 | 12,40 | 4,40 | 0,60 |
Typical mechanical properties all weld metal
| (*) |
Yield strength, N/mm2/MPa |
Tensile strength, N/mm2/MPa |
Elongation,% |
Impact work ISO-V KV J, – 10ºC |
| u | 950 | 1200 | 12 | 35 |
| a | 760 | 890 | 17 | 60 |
u - after welding, а - after annealing, 580ºС/8 h, cooling with furnace down to 300ºС, air
Available diameters and packaging
| Packing/diameter | Ø1,6mm | Ø2,0mm | Ø2,4mm | Ø3,0(3,2)mm |
| Cardboard box | 5 kg | 5 kg | 5 kg | 5 kg |
| Rod marking | HORDA 410NiMo | |||